Araldite 2015-1 is a toughened, two-component epoxy paste adhesive providing strong, weather-resistant bonds for GRP, SMC, metals, plastics, and dissimilar substrates.

  • Item Name: Araldite® 2015-1

  • Manufacturer: Huntsman Advanced Materials

  • Technologies: Two-component, room-temperature curing epoxy paste adhesive

  • Color: Beige (resin, hardener, and mixed)

  • Cure Type: Room temperature cure; accelerated with elevated temperature

  • Package Size: Contact to Techniq VN for details.

  • Shelf Life: Indicated on product label

1. Product Overview

Araldite® 2015-1 is a two-component, room temperature curing epoxy paste adhesive. It is thixotropic, toughened, and non-sagging up to 10 mm thickness, providing resilient bonds. It is specifically formulated for GRP, SMC, and dissimilar material bonding, with good resistance to weathering and environmental exposure.


2. Applications

  • Bonding glass-reinforced plastics (GRP) and sheet moulding compounds (SMC).

  • Suitable for metal-to-metal and plastic-to-plastic joints.

  • Useful in applications requiring gap filling, structural resilience, and durability under weathering conditions.

  • Applicable in transportation, construction, marine, and industrial sectors where toughened bonds are essential.

3. Typical Properties

Unmixed and Mixed

Property Resin (Part A) Hardener (Part B) Mixed Adhesive
Colour (visual) Beige paste Beige paste Beige paste
Specific Gravity 1.4 1.4 1.4
Viscosity at 25°C Thixotropic Thixotropic Thixotropic
Lap Shear Strength at 25°C > 15 MPa
Pot Life (100 g at 25°C) 45 – 55 min

Cured Properties (Typical)

Property Value Test Condition
Tensile Strength 31 MPa ISO 527, 16h cure at 40°C
Tensile Modulus 1600 MPa
Elongation at Break 4.2 %
Flexural Strength 43 MPa ISO 178
Flexural Modulus 1800 MPa
Shore Hardness (D scale) ~75 D (typical) Standard cured sample
Glass Transition Temperature 78°C (by DMA) Cure: 1h at 80°C
Shear Modulus G’ 1.8 GPa (-50°C), 1 GPa (0°C), 900 MPa (20°C), 540 MPa (50°C), 61 MPa (75°C), 12 MPa (100°C) ISO 6721

BERGQUIST microTIM mTIM 1028 Thermal Interface Coating High performance thermal management solution for nickel finished heat sinks, optical transceivers, and data center liquid cooling systems

BERGQUIST microTIM mTIM 1028 is purpose built for riding cage assemblies in servers, switches, and routers, interfacing with electroless nickel plated copper or aluminum heat sinks. It ensures stable operation in high power transceiver modules while also extending applicability to liquid cooling components, heat pipes, and fin based dissipative structures.

RELATED PRODUCT

Contact Technical Support

Leave your information or connect via Hotline, and our expert team will reach out immediately to provide professional consultation and customized solutions.

(+84) 889 901 929

Email: info@techniq.vn

Our Technical Support Team is on hand from 8:30 AM to 5:30 PM (GMT+7).

For requests outside these hours, please submit your request form and we will respond at the earliest opportunity.