LOCTITE HHD 3593

  • Item Name: LOCTITE HHD 3593
  • Manufacturer: Henkel
  • Product category: Hot Melt Adhesive
  • Technologies: Polyurethane Hot Melt (Reactive polyurethane)
  • Applications: Ideal for device assembly in automated or manual production lines.
  • Color: Black Solid
  • Cure type: Solidification and Moisture
  • Package size: Contact to Techniq VN for details
  • Shelf life: 365 days

1. Product Overview

LOCTITE HHD 3593 is a black polyurethane hot melt adhesive that cures with moisture. It is designed for device assembly, offering a long open time and high handling strength immediately after bonding. This one-part adhesive requires no mixing.

2. Applications

  • Used in device assembly
  • Suitable for automatic and manual assembly lines

3. Typical Properties

Property Value
Appearance Black Solid
Technology Polyurethane Hot Melt
Solids Content 100%
Components One part (no mixing required)
Curing Method Solidification & Moisture
Viscosity (100°C, mPa·s) 5,400 (Brookfield – Thermosel)
Density @ 25°C (g/cm³) 1.1
Shelf Life @ 5-25°C (days) 365
Flash Point See SDS

4. Curing Performance

Parameter Value
Open Time @ 25°C (minutes) >6
Preheating Schedule 20 – 30 mins @ 100°C
Application Temperature (°C) 100 – 110
Final Strength Development 1 – 5 days (moisture-dependent)

Curing is influenced by:

  • Humidity in the environment
  • Moisture content of substrates
  • Substrate permeability
  • Adhesive layer thickness

5. Performance After Curing (Tested at 23 ±5°C, 50 ±5% RH)

Test Condition Adhesion Strength (N/mm²)
Tensile Adhesion (Glass to Steel) After 1 hour 0.819
After 24 hours 2.42

RELATED PRODUCT

Contact Technical Support

Leave your information or connect via Hotline, and our expert team will reach out immediately to provide professional consultation and customized solutions.

(+84) 889 901 929

Email: info@techniq.vn

Our Technical Support Team is on hand from 8:30 AM to 5:30 PM (GMT+7).

For requests outside these hours, please submit your request form and we will respond at the earliest opportunity.